DuPont Performance Polymers Zytel® 8018HS BKB085 Nylon 66 (Unverified Data**) 物性表
物理性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
比重 |
1.19 g/cc |
1.19 g/cc |
DAM; ASTM D792 |
密度 |
1.19 g/cc |
0.0430 lb/in³ |
DAM; ISO 1183 |
填料含量 |
14 % |
14 % |
DAM |
机械性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
洛氏硬度(M 级) |
70 |
70 |
DAM; ISO 2039/2 |
洛氏硬度(R 级) |
110 |
110 |
DAM; ISO 2039/2 |
抗张强度(断裂) |
85.0 MPa @Temperature 23.0 °C |
12300 psi @Temperature 73.4 °F |
DAM; ISO 527 |
抗张强度 |
90.0 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
DAM; ASTM D638 |
伸长率 (断裂) |
6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
DAM; ASTM D638 |
|
9.0 % @Temperature 23.0 °C |
9.0 % @Temperature 73.4 °F |
DAM; ISO 527 |
拉伸模量 |
4.20 GPa @Temperature 23.0 °C |
609 ksi @Temperature 73.4 °F |
DAM; ISO 527 |
弯曲模量 |
3.60 GPa @Temperature 23.0 °C |
522 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
|
3.66 GPa @Temperature 23.0 °C |
531 ksi @Temperature 73.4 °F |
DAM; ASTM D790 |
悬壁梁缺口冲击强度 |
1.40 J/cm @Temperature 23.0 °C |
2.62 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 |
悬壁梁无缺口冲击强度 |
9.60 J/cm @Temperature 23.0 °C |
18.0 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D4812 |
悬壁梁缺口冲击强度 |
7.00 kJ/m² @Temperature -40.0 °C |
3.33 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A |
|
13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
简支梁缺口冲击强度 |
0.400 J/cm² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA |
|
1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
电气性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
相比耐漏电起痕指数(CTI) |
580 V @Temperature 23.0 °C |
580 V @Temperature 73.4 °F |
DAM; UL 746A |
热性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
线形热膨胀系数 - 流动 |
500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 |
|
500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
|
500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
DAM; ASTM E 831 |
|
500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 |
|
500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 |
|
500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 |
线性热膨胀系数,横向流动 |
96.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
53.3 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ASTM E 831 |
|
96.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
53.3 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 |
|
118 µm/m-°C @Temperature 23.0 - 55.0 °C |
65.6 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
|
118 µm/m-°C @Temperature 23.0 - 55.0 °C |
65.6 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 |
|
123 µm/m-°C @Temperature 55.0 - 160 °C |
68.3 µin/in-°F @Temperature 131 - 320 °F |
DAM; ASTM E 831 |
|
123 µm/m-°C @Temperature 55.0 - 160 °C |
68.3 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 |
熔融温度 |
263 °C |
505 °F |
10°C/min; DAM; ISO 11357-1/-3 |
|
263 °C |
505 °F |
DAM; ASTM D3418 |
载荷下热变形温度(0.46 MPa) |
246 °C |
475 °F |
DAM; ISO 75-1/-2 |
载荷下热变形温度(1.8 MPa) |
195 °C |
383 °F |
DAM; ISO 75-1/-2 |
|
205 °C |
401 °F |
DAM; ASTM D648 |
UL RTI |
120 °C @Thickness 3.00 mm |
248 °F @Thickness 0.118 in |
DAM; UL 746B |
|
120 °C @Thickness 1.50 mm |
248 °F @Thickness 0.0591 in |
DAM; UL 746B |
|
120 °C @Thickness 0.750 mm |
248 °F @Thickness 0.0295 in |
DAM; UL 746B |
UL RTI,机械冲击 |
65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
DAM; UL 746B |
|
95.0 °C @Thickness 1.50 mm |
203 °F @Thickness 0.0591 in |
DAM; UL 746B |
|
105 °C @Thickness 3.00 mm |
221 °F @Thickness 0.118 in |
DAM; UL 746B |
UL RTI,机械无冲击 |
85.0 °C @Thickness 0.750 mm |
185 °F @Thickness 0.0295 in |
DAM; UL 746B |
|
105 °C @Thickness 1.50 mm |
221 °F @Thickness 0.0591 in |
DAM; UL 746B |
|
105 °C @Thickness 3.00 mm |
221 °F @Thickness 0.118 in |
DAM; UL 746B |
可燃性(UL94) |
HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
DAM; IEC 60695-11-10 |
|
HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 |
|
HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; IEC 60695-11-10 |
|
HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; UL94 |
|
HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; UL94 |
|
HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
DAM; UL94 |
加工性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
加工(熔体)温度 |
295 °C |
563 °F |
DAM; Optimum |
|
285 - 305 °C |
545 - 581 °F |
DAM |
模具温度 |
50.0 - 100 °C |
122 - 212 °F |
DAM |
|
80.0 °C |
176 °F |
DAM; optimum |
干燥温度 |
80.0 °C |
176 °F |
DAM |
干燥时间 |
2.00 - 4.00 hour |
2.00 - 4.00 hour |
DAM |
水分含量 |
<= 0.20 % |
<= 0.20 % |
DAM |
材料描述 |
|
测试方法 |
添加剂 |
Heat Stabilizer |
DAM |
外观 |
Black Color |
DAM |
|
Colors Available |
DAM |
Drying Recommended |
Yes, if moisture content of resin exceeds recommended level |
DAM |
特性 |
Impact Resistance, High |
DAM |
|
Toughness, Good |
DAM |
Filler |
Glass fiber reinforcement |
DAM |
形式 |
Pellets |
DAM |
Generic |
Nylon 66 |
DAM |
Heat Stabilized |
Yes |
DAM |
Material Status |
Current |
DAM |
部件标识代码 |
>PA66-IGF14< |
ISO 11469; DAM |
Polymer Family |
Polyamide |
DAM |
Polymer Type |
PA66 |
DAM |
加工方法 |
Injection Molding |
DAM |
产品分类 |
Glass Reinforced Resins |
DAM |
|
Toughened Resins |
DAM |
树脂识别 |
PA66-IGF14 |
ISO 1043; DAM |
符合RoHS指令 |
Contact Manufacturer |
DAM |
Ultrasonic Weldable |
Yes |
DAM |
用途 |
Appliance Components |
DAM |
|
Automotive Applications |
DAM |
|
Fasteners |
DAM |
|
Industrial Applications |
DAM |
|
Sporting Goods |
DAM |