PCTG材料 DN001 Eastman Tritan 共聚聚酯 伊斯曼官方datasheet物性表 TDS
PCTG材料 Eastman Tritan 共聚聚酯 DN001 伊斯曼官方物性表 TDS
与我们联系索取Eastman官方 DN001 物性表 datasheet
PCTG 美国伊斯曼Eastar™ DN001, Natural
Copolyester
Eastman Chemical Company
产品说明：
Eastar™ copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. DN001 is a base material without mold release or ultra-violet inhibitors(UVI).
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.
物性信息：
|
基本信息 |
|
|
黄卡编号 |
|
|
特性 |
|
|
用途 |
|
|
外观 |
|
|
形式 |
|
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
|
|
|
|
-- |
1.23 |
g/cm³ |
ASTM D792 |
|
23°C |
1.23 |
g/cm³ |
ISO 1183 |
|
收缩率 - 流动 (3.20 mm) |
0.20 到 0.50 |
% |
ASTM D955 |
|
吸水率 (23°C, 24 hr) |
0.13 |
% |
ASTM D570, ISO 62 |
|
硬度 |
额定值 |
单位制 |
测试方法 |
|
洛氏硬度 (R 级, 23°C) |
105 |
|
ASTM D785 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 (23°C) |
1800 |
MPa |
ASTM D638 |
|
抗张强度 |
|
|
|
|
屈服, 23°C |
45.0 |
MPa |
ASTM D638 |
|
屈服, 23°C, 4.00 mm |
46.0 |
MPa |
ISO 527-2 |
|
断裂, 23°C |
52.0 |
MPa |
ASTM D638 |
|
断裂, 23°C, 4.00 mm |
47.0 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
屈服, 23°C |
5.0 |
% |
ASTM D638 |
|
屈服, 23°C, 4.00 mm |
4.4 |
% |
ISO 527-2 |
|
断裂, 23°C |
330 |
% |
ASTM D638 |
|
断裂, 23°C, 4.00 mm |
230 |
% |
ISO 527-2 |
|
弯曲模量 |
|
|
|
|
23°C |
1800 |
MPa |
ASTM D790 |
|
23°C, 4.00 mm |
1800 |
MPa |
ISO 178 |
|
弯曲应力 |
|
|
|
|
23°C, 4.00 mm |
63.0 |
MPa |
ISO 178 |
|
屈服, 23°C |
66.0 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
-40°C |
64 |
J/m |
ASTM D256 |
|
23°C |
无断裂 |
|
ASTM D256 |
|
-40°C |
7.4 |
kJ/m² |
ISO 180 |
|
23°C |
130 |
kJ/m² |
ISO 180 |
|
无缺口悬臂梁冲击 |
|
|
ASTM D4218 |
|
-40°C |
无断裂 |
|
ASTM D4218 |
|
23°C |
无断裂 |
|
ASTM D4218 |
|
多轴向仪器化冲击能量 |
|
|
ISO 6603-2 |
|
-40°C, 能量到力量峰值 |
16.0 |
J |
ISO 6603-2 |
|
23°C, 能量到力量峰值 |
14.0 |
J |
ISO 6603-2 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
载荷下热变形温度 |
|
|
|
|
0.45 MPa, 未退火 |
74.0 |
°C |
ASTM D648, ISO 75-2/B |
|
1.8 MPa, 未退火 |
64.0 |
°C |
ASTM D648 |
|
1.8 MPa, 未退火 |
65.0 |
°C |
ISO 75-2/A |
|
维卡软化温度 |
|
|
|
|
-- |
88.0 |
°C |
ASTM D1525, ISO 306/A 3 1 |
|
-- |
79.0 |
°C |
ISO 306/B |
|
比热 |
|
|
|
|
60°C |
1340 |
J/kg/°C |
|
|
240°C |
2050 |
J/kg/°C |
|
|
导热系数 (23°C) |
0.19 |
W/m/K |
|
|
电气性能 |
额定值 |
单位制 |
测试方法 |
|
介电强度 (23°C) |
16 |
kV/mm |
ASTM D149 |
|
介电常数 |
|
|
ASTM D150 |
|
23°C, 1 kHz |
2.70 |
|
ASTM D150 |
|
23°C, 10 kHz |
2.70 |
|
ASTM D150 |
|
23°C, 100 kHz |
2.60 |
|
ASTM D150 |
|
23°C, 1 MHz |
2.50 |
|
ASTM D150 |
|
耗散因数 |
|
|
ASTM D150 |
|
23°C, 1 kHz |
5.6E-3 |
|
ASTM D150 |
|
23°C, 10 kHz |
0.012 |
|
ASTM D150 |
|
23°C, 100 kHz |
0.016 |
|
ASTM D150 |
|
23°C, 1 MHz |
0.018 |
|
ASTM D150 |
|
耐电弧性 |
66.0 |
sec |
ASTM D495 |
|
可燃性 |
额定值 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
UL 94 |
|
1.60 mm |
HB |
|
UL 94 |
|
3.20 mm |
HB |
|
UL 94 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
71.0 |
°C |
|
|
干燥时间 |
6.0 |
hr |
|
|
加工（熔体）温度 |
250 到 270 |
°C |
|
|
模具温度 |
15.0 到 40.0 |
°C |
|
Tritan™，全称Tritan Copolyester，中文名萃特， 是美国Eastman公司开发的新一代共聚酯。
例如，聚碳酸酯水解后会产生双酚A。现代医学研究认为，双酚A超过一定剂量或将影响人类健康（包括动物）， 如果长期摄入微量的双酚A，会造成内分泌系统混乱，非常有可能对生殖系统产生不良影响，破坏性别比例的平衡，因此部分国家和地区已经限制或禁用聚碳酸酯。
Tritan™的优点
1.不含BPA：伊斯曼Tritan™“在聚合生产过程中无BPA成分,在使用过程中也不会释放BPA，符合环保要求及FDA。
2.清晰透明：透光率>90%，雾度<1%，有水晶般的光泽。
3.优异的抗冲击强度：无缺口冲击不断,有缺口冲击强度因牌号不同在650-980J/m之间，可比美PC的冲击强度。•优秀的抗化、抗水解性能：Tritan ™"能抗洗涤剂、清洁剂、经类溶剂、油类、香水等腐蚀:在湿热的环境中能抗水解。
4.耐温高：低压热变形温度(HDT@0.455MPa)根据牌号不同在94℃-109℃之间。
5.流动性好：测试条件在2.16kgf压力,280熔体温度条件下,烧指(MI)根据牌号不同在15.3-29.5之间。
·容易成型加工：Tritan ™“的牌号可用注塑(injection)、挤出(extrusion)、吹塑(EEM)、注拉吹(ISBM)等各种方法加工。一般来说，用PC能正常生产的模具，无须改动便可用Tritan™”“来生产，生产周期时间非常接近。
6.容易二次加工：PCTG Tritan 可适用于的二次加工方法包括:UV胶水粘接、超声波熔接、表面印刷喷漆、表面真空电镀等。
7.制品残余应力小：注塑后，产品残余应力比PC小，无须再做后续退火处理。产品在使用过程中由于残余应力开裂的机会少，所以Tritan™制造出来的产品更加经久耐用。
Tritan™的市场应用
伊斯曼 PCTG Tritan™ 作为新一代共聚聚酯，经过Eastman多年的研发，已进入商业化应用阶段。其牌号已自成体系，以满足市场的各种需求。Eastman首先在欧美市场上进行了推广应用，Tritan TM凭着环保易加工等优良品质引起了欧美市场的积极响应，并取得了很大的成功。总体来说，Tritan™"可以适用于传统共聚聚酯的所有市场应用。在这里，我们将通过案例展示来着重介绍它替代PC的市场应用。
PCTG 美国伊斯曼 Eastman 共聚聚酯材料 Eastman Tritan 专业PCTG PETG PCTA 高温PCTG供应商